EFFECT OF DOUBLE HEATING OF THE NEAR-SEAM SECTION IN THE THERMAL IMPACT ZONE ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF K60 STRENGTH CLASS STEEL WITH INCREASED DEFORMABILITY
UDC: 621.791.011:539.3
DOI: 10.33285/1999-6934-2021-1(121)-23-27
Authors:
UTKIN IVAN YURIEVICH1,
PONOMARENKO DARYA VIKTOROVNA1
1 National University of Oil and Gas "Gubkin University", Moscow, Russian Federation
Keywords: kinetics of austenite phase transformations; heat-affected near-seam sector of zone; steel with increased deformation capacity
Annotation:
The features of austenite kinetics decomposition in the near-seam section of heat-affected zones of steel with high strain capacity at the cooling rate typical of welding under flux are studied. The values of metal mechanical properties at different heating temperatures of this section are determined.
Bibliography:
1. Освоение производства труб большого диаметра с повышенной деформационной способностью / И.Ю. Пышминцев, А.О. Струин, А.М. Гервасьев [и др.] // Вестн. ЮУрГУ. Сер. Металлургия. – 2016. – Т. 16, № 1. – С. 82–90. – DOI: 10.14529/met160112
2. Особенности многоэлектродной сварки под слоем флюса при производстве высокопрочных толстостенных труб / А.Н. Борцов, И.П. Шабалов, А.А. Величко [и др.] // Металлург. – 2013. – № 4. – С. 69–76.
3. Взаимосвязь тепловых процессов с морфологией сварных соединений и перспективные виды сварки применительно к толстостенным электросварным трубам / А.А. Величко, А.Н. Борцов, И.П. Шабалов [и др.] // Металлург. – 2014. – № 3. – С. 72–77.
4. СТО Газпром 2-2.3-137-2007. Инструкция по технологиям сварки при строительстве и ремонте промысловых и магистральных газопроводов. Часть II. – Введ. 2007–12–14. – М.: ИРЦ газовой промышленности, 2007.
Back to issue